US 12,453,960 B1
Nanocomposite material fabrication
Ehab Abdelhamed Abdelrahman Ahmed, Riyadh (SA); and Babiker Yagoub Elhadi Abdulkhair, Riyadh (SA)
Assigned to IMAM MOHAMMAD IBN SAUD ISLAMIC UNIVERISTY, Riyadh (SA)
Filed by IMAM MOHAMMAD IBN SAUD ISLAMIC UNIVERSITY, Riyadh (SA)
Filed on Mar. 6, 2025, as Appl. No. 19/072,950.
Int. Cl. B01J 23/06 (2006.01); B01J 20/04 (2006.01); B01J 20/06 (2006.01); B01J 20/28 (2006.01); B01J 20/30 (2006.01); B01J 21/06 (2006.01); B01J 21/18 (2006.01); B01J 23/02 (2006.01); B01J 35/30 (2024.01); B01J 35/39 (2024.01); B01J 35/40 (2024.01); B01J 35/45 (2024.01); B01J 35/51 (2024.01); B01J 35/77 (2024.01); B01J 37/04 (2006.01); B01J 37/08 (2006.01); C02F 1/28 (2023.01); C02F 101/20 (2006.01); C02F 101/30 (2006.01)
CPC B01J 23/06 (2013.01) [B01J 20/041 (2013.01); B01J 20/06 (2013.01); B01J 20/28004 (2013.01); B01J 20/28007 (2013.01); B01J 20/28019 (2013.01); B01J 20/3078 (2013.01); B01J 20/3085 (2013.01); B01J 21/063 (2013.01); B01J 21/18 (2013.01); B01J 23/02 (2013.01); B01J 35/39 (2024.01); B01J 35/394 (2024.01); B01J 35/40 (2024.01); B01J 35/45 (2024.01); B01J 35/51 (2024.01); B01J 35/77 (2024.01); B01J 37/04 (2013.01); B01J 37/084 (2013.01); C02F 1/288 (2013.01); C02F 1/281 (2013.01); C02F 2101/20 (2013.01); C02F 2101/30 (2013.01)] 20 Claims
OG exemplary drawing
 
1. A Mg0.6Ti2.4O5/MgTiO3/tetragonal TiO2/orthorhombic TiO2/CdO/C nanocomposite material, comprising:
an orthorhombic Mg0.6Ti2.4O5 phase;
a hexagonal MgTiO3 phase;
a tetragonal TiO2 phase;
a cubic CdO phase; and
an orthorhombic TiO2 phase,
wherein the Mg0.6Ti2.4O5/MgTiO3/tetragonal TiO2/orthorhombic TiO2/CdO/C nanocomposite material has a granular morphology comprising spherical particles having an average particle diameter in a range from 50 to 130 nm.