CPC C08F 110/02 (2013.01) [C08F 8/22 (2013.01); C08L 23/286 (2013.01); C08F 4/6592 (2013.01); C08F 4/76 (2013.01); C08F 8/20 (2013.01); C08F 2500/07 (2013.01); C08F 2500/12 (2013.01); C08F 2500/18 (2013.01); C08F 2810/20 (2013.01)] | 20 Claims |
1. A polyethylene satisfying the following conditions 1) to 4):
1) a relaxation time is 2 seconds or less,
2) a melt index MI5 (a melt index of the polyethylene measured at a temperature of 190° C. under a load of 5 kg in accordance with ASTM D 1238) is 0.75 g/10 min to 1.2 g/10 min,
3) a melt flow rate ratio (MFRR21.6/5, a value obtained by dividing the melt index measured at 190° C. under a load of 21.6 kg by the melt index measured at 190° C. under a load of 5 kg in accordance with ASTM D 1238) is 9.5 to 12.5, and
4) a density is 0.947 g/cm3 to 0.954 g/cm3.
|