CPC C09D 127/16 (2013.01) [B05D 7/14 (2013.01); C09D 5/00 (2013.01); C09D 7/40 (2018.01); C09D 7/61 (2018.01); C09D 7/69 (2018.01); B05D 5/083 (2013.01); B05D 2601/00 (2013.01); B05D 2602/00 (2013.01); C08K 3/36 (2013.01); C08K 2201/005 (2013.01); C08L 27/18 (2013.01)] | 7 Claims |
1. A coil-coated article, comprising
a substrate;
a coating disposed thereon at a film thickness of 0.5 to 1 mil and cured by baking for 8 to 25 seconds to a peak metal temperature (PMT) of about 200 to 250° C., the coating derived from a composition comprising:
a binder system including a first resin component comprising at least a fluoropolymer;
an organic filler material comprising polytetrafluoroethylene (PTFE) having a D50 particle size of about 7 to 12 μm;
about 1.5 to 10 wt %, based on the total weight of the composition, of an inorganic filler material comprising untreated amorphous silica and having a D50 particle size of about 5 to 15 μm; and
a liquid carrier,
wherein the coated article demonstrates damage tolerance of at least about 10,000 cycles at a coefficient of friction (μ) of no more than about 0.15.
|