CPC G02B 5/226 (2013.01) [B32B 17/10045 (2013.01); B32B 17/10064 (2013.01); B32B 17/10119 (2013.01); B32B 17/10137 (2013.01); C03B 5/173 (2013.01); C03C 1/004 (2013.01); C03C 3/083 (2013.01); C03C 3/085 (2013.01); C03C 3/095 (2013.01); C03C 4/082 (2013.01); C03C 4/10 (2013.01); F41H 5/0407 (2013.01); G02B 13/14 (2013.01); B32B 2307/412 (2013.01); B32B 2605/08 (2013.01); B32B 2605/18 (2013.01); C03C 10/0027 (2013.01); C03C 21/002 (2013.01); C03C 2204/00 (2013.01); Y02P 40/57 (2015.11)] | 8 Claims |
1. A low infrared absorbing (LIRA) glass composition comprising:
| ||||||||||||||||||||||||||||||||||||||||||||||||||||
an oxidizer selected from the group of cerium oxide in the range of greater than 0 to 0.50 wt % and/or manganese oxide in the range of greater than 0 to 0.75 wt %;
less than 5 wt % of additional glass forming materials and glass modifiers or colorants, selected from the group of MgO, CaO, MnO, TiO2, Sb2O3, As2O3, K2O, PbO, SO3, colorants and mixtures thereof; and
a redox ratio in the range of 0.005-0.15, wherein glass formed from the glass composition and having a thickness of 0.223 inch (5.7 millimeters) has:
a visible transmission over a wavelength range of 380 to 780 nm of equal to or greater than 88%;
an infrared transmission over a wavelength range of 800 to 2100 nm of equal to or greater than 80%; and
an infrared viewing transmission over the wavelength range of 400 to 920 nm of equal to or greater than 80%.
|