CPC B01J 29/70 (2013.01) [B01J 23/883 (2013.01); B01J 29/06 (2013.01); B01J 29/061 (2013.01); B01J 29/064 (2013.01); B01J 29/076 (2013.01); B01J 29/106 (2013.01); B01J 29/126 (2013.01); B01J 29/146 (2013.01); B01J 29/166 (2013.01); B01J 29/72 (2013.01); B01J 29/74 (2013.01); B01J 29/76 (2013.01); B01J 29/80 (2013.01); B01J 35/006 (2013.01); B01J 35/0006 (2013.01); B01J 35/0046 (2013.01); B01J 35/109 (2013.01); B01J 35/1057 (2013.01); B01J 35/1061 (2013.01); B01J 37/0201 (2013.01); B01J 37/04 (2013.01); B01J 37/08 (2013.01); B01J 37/10 (2013.01); C01B 39/02 (2013.01); C01B 39/46 (2013.01); C01B 39/48 (2013.01); C01B 39/52 (2013.01); B01J 23/42 (2013.01); B01J 2029/062 (2013.01); B01J 2229/18 (2013.01); B01J 2229/183 (2013.01); B01J 2229/186 (2013.01); B01J 2229/42 (2013.01); C10G 11/05 (2013.01)] | 11 Claims |
1. A method of producing a hydrocracking catalyst, in which the method comprises:
adding sodium hydroxide, an aluminum compound, a salt having an anion and a cation, and a silicon compound to an aqueous solution to form an aqueous mixture;
stirring the aqueous mixture;
adding a platinum compound to the aqueous mixture to form a pre-catalyst mixture;
heating the pre-catalyst mixture at from 80° C. to 200° C. for at least 24 hours, thereby crystalizing the pre-catalyst mixture to form the hydrocracking catalyst comprising platinum encapsulated zeolite.
|