CPC C08F 265/06 (2013.01) [C08F 220/14 (2013.01); C08F 220/286 (2020.02); C08F 283/06 (2013.01); C08L 13/02 (2013.01); C09D 151/003 (2013.01)] | 15 Claims |
1. An aqueous latex composition comprising an acrylic core-shell latex, wherein acrylic monomers are present at greater than 95% of all film forming monomers and wherein a water-retaining monomer is copolymerized to the shell,
wherein the Tg of the core ranges from about 0° C. to about 12° C., the Tg of the shell ranges from about 13° C. to about 40° C.,
wherein the mean volume average particle size of the core-shell latex ranges from about 125 nm to about 200 nm, and
wherein the core-shell latex comprises at least one acrylic monomer having a solubility that ranges from about 10 g/L to about 30 g/L at 30° C., and present in the shell polymer in an amount greater than about 50 wt. % of all monomers in the shell, and
wherein the water-retaining monomer is present in the shell in an amount from about 1.43% to about 5% by weight of the core-shell latex.
|