CPC C22C 1/0425 (2013.01) [B22F 3/172 (2013.01); B22F 3/20 (2013.01); B22F 9/04 (2013.01); B22F 9/082 (2013.01); B22F 9/22 (2013.01); C22C 1/05 (2013.01); C22C 9/00 (2013.01); C22C 32/0021 (2013.01); B22F 2009/043 (2013.01); B22F 2301/10 (2013.01); B22F 2302/253 (2013.01)] | 10 Claims |
1. A brief manufacturing process of a nano dispersion copper alloy, comprising the steps of:
preparing Cu—Al2O3 alloy powder by an internal oxidation method;
mixing the Cu—Al2O3 alloy powder with Cu—Ca—La alloy powder;
sheathing the mixed powder under protection of argon to obtain a sheath;
performing hot extrusion on the sheath at 900° C. to 920° C. to obtain an extruded sheath;
performing rotary forging on the extruded sheath to obtain a rotationally forged bar;
placing the rotationally forged bar in a new sheath;
vacuumizing the new sheath to be less than or equal to 10−3 Pa;
sealing the new sheath to obtain a new sealed sheath; and
placing the new sealed sheath in a nitrogen atmosphere with a temperature ranging from 450° C. to 550° C. and a pressure intensity ranging from 40 Mpa to 60 Mpa for 3 hours to 5 hours,
wherein the nano dispersion copper alloy comprises the following components in percentage by mass:
0.05 wt. % to 1.61 wt. % of Al2O3,
0.008 wt. % to 0.012 wt. % of Ca,
0.008 wt. % to 0.012 wt. % of La, and the balance of Cu.
|