CPC H01M 4/364 (2013.01) [C01G 53/50 (2013.01); H01M 4/505 (2013.01); H01M 4/525 (2013.01); H01M 4/5825 (2013.01); H01M 4/623 (2013.01); H01M 4/625 (2013.01); H01M 10/0525 (2013.01); C01P 2004/50 (2013.01); C01P 2004/51 (2013.01); C01P 2004/61 (2013.01); C01P 2004/62 (2013.01); C01P 2006/11 (2013.01); C01P 2006/12 (2013.01); C01P 2006/14 (2013.01); C01P 2006/40 (2013.01); H01M 2004/028 (2013.01)] | 10 Claims |
1. Process for making a lithiated transition metal oxide, said process comprising the following steps:
(a) providing a precursor selected from mixed oxides, mixed hydroxides, mixed oxyhydroxides, and mixed carbonates of nickel and at least one transition metal selected from manganese and cobalt, wherein at least 45 mole-% of the cations of the precursor are Ni cations,
(b) mixing said precursor with a lithium salt and the lithium salt is Li2CO3, thereby obtaining a mixture,
(c) adding at least one phosphorus compound of general formula (I)
XyH3-yPO4 (I)
wherein:
X is selected from NH4 and Li,
y is 1 or 2,
to the mixture obtained in step (b),
wherein steps (b) and (c) may be performed consecutively or simultaneously,
(d) treating the mixture so obtained at a temperature in the range of from 650 to 950° C.; and
wherein step (d) is performed in an atmosphere of oxygen or oxygen-enriched air.
|