CPC C03C 14/004 (2013.01) [C03C 3/089 (2013.01); C03C 4/16 (2013.01); C03C 12/00 (2013.01); H01B 3/087 (2013.01); H01B 3/12 (2013.01); C03C 2204/00 (2013.01); C03C 2214/04 (2013.01); C03C 2214/30 (2013.01)] | 6 Claims |
1. A glass powder, which is formed of alkali borosilicate glass, wherein the glass powder comprises 0.1 mol % to 1.0 mol %, provided that 1.0 mol % is excluded, of Li2O+Na2O+K2O in a glass composition, has a molar ratio Li2O/(Li2O+Na2O+K2O) of from 0.35 to 0.65, a molar ratio Na2O/(Li2O+Na2O+K2O) of from 0.3 to 0.55, and a molar ratio K2O/(Li2O+Na2O+K2O) of from 0.025 to 0.15, and has a specific dielectric constant at 25° C. and 16 GHz of from 3.5 to 4.0 and a dielectric dissipation factor at 25° C. and 16 GHz of 0.0020 or less.
|