US 11,862,810 B2
Separator for electrochemical element
Hiroki Cho, Ibaraki (JP); Yoshinori Sato, Ibaraki (JP); Ayuka Noguchi, Ibaraki (JP); Akihiko Kawano, Ibaraki (JP); Masanao Tanaka, Ibaraki (JP); and Yasuhiro Ito, Tokyo (JP)
Assigned to JAPAN VILENE COMPANY, LTD., Tokyo (JP)
Filed by JAPAN VILENE COMPANY, LTD., Tokyo (JP)
Filed on Apr. 8, 2022, as Appl. No. 17/716,776.
Application 17/716,776 is a continuation of application No. 16/631,408, abandoned, previously published as PCT/JP2018/026772, filed on Jul. 17, 2018.
Claims priority of application No. 2017-139501 (JP), filed on Jul. 18, 2017.
Prior Publication US 2022/0231377 A1, Jul. 21, 2022
Int. Cl. H01M 50/44 (2021.01); H01M 50/429 (2021.01); H01M 50/449 (2021.01); H01M 50/491 (2021.01); H01M 50/423 (2021.01); H01M 50/414 (2021.01); H01M 50/454 (2021.01); H01M 50/451 (2021.01)
CPC H01M 50/44 (2021.01) [H01M 50/423 (2021.01); H01M 50/4295 (2021.01); H01M 50/449 (2021.01); H01M 50/491 (2021.01); H01M 50/414 (2021.01); H01M 50/451 (2021.01); H01M 50/454 (2021.01)] 5 Claims
OG exemplary drawing
 
1. A method for preparing a separator for an electrochemical element, comprising the following steps:
(1) a step of preparing a nonwoven fabric containing second short fibers as the constituent fibers wherein fibers in the nonwoven fabric are adhered to each other by the second short fibers without using a binder;
(2) a step of forming a dispersion containing first short fibers and pulp-like fibers in a dispersion medium on one main surface of the nonwoven fabric, and sucking and removing the dispersion medium from the other main surface side of the nonwoven fabric, to form a fiber deposit layer on the one main surface of the nonwoven fabric, wherein the first short fibers and the pulp-like fibers are mixed with each other, and some of the first short fibers and the pulp-like fibers penetrates into the nonwoven fabric; and
(3) a step of drying a laminate comprising the fiber deposit layer formed on the one main surface of the nonwoven fabric,
wherein:
the separator for an electrochemical element comprises a fibrous structure;
the fibrous structure has a first fibrous layer part in which the first short fibers and pulp-like fibers are intertwined with each other, and a second fibrous layer part derived from the nonwoven fabric in which the fibrous structure comprises the second short fibers;
the first short fibers comprised in the first fibrous layer part are fibers comprising at least one resin selected from the group consisting of polyester resins, polyolefin resins and nylon resins;
the first short fibers comprised in the first fibrous layer part adhere the first short fibers and/or the pulp-like fibers composing the first fibrous layer part to each other by heating;
the second short fibers comprised in the second fibrous layer part adhere the constituent fibers composing the second fibrous layer part to each other without melting of the second short fibers by pressing in addition to heating;
some of the first short fibers and the pulp-like fibers constituting the first fibrous layer part penetrates the second fibrous layer part; and
a pore diameter distribution of the fibrous structure satisfies the following formula:
0 μm<Dmax<18 μm, and
0 μm≤(Dmax−Dave)<13 μm,
wherein Dmax is a maximum pore diameter (μm) of the fibrous structure, and Dave is an average pore diameter (μm) of the fibrous structure.